Generally speaking, you want to be at about a 400 grit finish or better to get an even etch across the pattern. Muriatic also contains some other stuff, typically iron, which is already starting to become ferric. Will muriatic acid be abel to etch Damascus steel if so how long should I leave it in for? It looks good, but provides little function. Remove the steel plate and clean it. Anything works. Two popular acids to use are Muriatic acid or feric chloride. Update It's often used in swimming pools to lower the pH of the water. It is an ultra high carbon steel that achieved liquid state which should, theoretically, allow you to get a . OP. Main Menu. Voil #damasteelab #damasteel #damascus #etching #HCl #muriatic #acid #BjrkmansTwist #knife #knifeblade 1. Share Facebook; Twitter; Linkedin; copy link. Archived. M. michiganroadkill OP. If you want a deeper etch, repeat steps 5 and 6. The muriatic is available at big box home improvement stores or pool supply stores. It fumes a lot (toxic) and the fumes will rust everything in your shop. If you are using hydrochloric acid, you can set the particle size of Damascus to 1200 or keep it to 400. It still retains enough corrosive quality to etch your steel blades. I am worried that the 416 might react differently to the muriatic acid than the Mike norris damascus. Thanks . In order to achieve a perfect etching result, the following steps should be followed. My favorite supplier of muriatic acid is any place that carries pool supplies. Choose the type of steel you want to etch. Since it can get into the layers and the blade keeps rusting. Save Comment CaiLei. Adaugat pe februarie 27, 2021 . How do you etch with muriatic acid? Step 1: Sanding Bring your damascus blade (hardened) to a 400, 600 or higher up to 1200 grit hand satin finish depending on your personal preference. Etching of Damascus is done after manufacturing or grinding of the blank to bring out the contrasting steel patterns. If you are having trouble getting Ferric, try using Muriatic. Which type of steel you etch will determine the best acid or chemical to use to etch it with. Official website of historian Rick Perlstein, author of Before The Storm, Nixonland, The Invisible Bridge and Reaganland Acid; Etch; HCL; Muriatic Acid; Hydrochloric Acid; Design; By Luke March, October 23, 2012 in Finishes for Metal. The video shows the process we used to mask off the important areas, what acids we used, and how we did it. Since I don't have access to ferric chloride and it seems dangerous and expensive I was wondering if I could just dip my blade into coffee and . Posted by Richard Ranney on July 2, 2021, 9:54 pm, in reply to "Re: Hydrochloric or Muriatic acid on Damascus " It also eats at the steel. Vinegar etching on damascus blades is. Do not change before creativity! Muriatic Acid, Ferric Chloride, Radio Shack PCB Etchant (Computer board etching solution) and I have heard even Coke a Cola. For detailed instructions for etching Damascus, use this link. Advice on etching aluminum with muriatic acid. It is a corrosive salt. It is in a greatly reduced concentration compared to the 30% hydrochloric acid (muriatic acid). Nitric Acid - mixture of 5 - 10% nitric acid with the balance being alcohol. . Campfire Guide. Adaugat pe februarie 27, 2021 . Ferric chloride is not an "acid" per se. Followers 0. . Register Log In Home Forums Knives and Blades etching damascus: Forums User List Calendar Active Threads Forum Help: Previous Thread: Next Thread : Print Thread: Hop To : etching damascus #12921123 06/14/18: Joined: Dec 2004. by Levi Alston. We've used Muriatic Acid in the past . This is commonly sold in home improvement stores and pool supply stores in gallon jugs. My first thought was to use 416 pins, peen them in, sand them smooth and then etch along with the rest of the knife. I am planning on using some Mike Norris stainless damasus for the bolsters on a stainless damascus blade. 3. Need help with etching Damascus. First attempts at Acid Etching. How to etch stainless steel and carbon Damascus steel. Sand your Damascus to 400 to 600 grit. Posted by 1 year ago. Do not polish before etching! Warm your acid to room temperature. When you are happy with how deep the etch is and have done the final scrubbing, dip it in the acetone, allow to dry then give it another 3 minutes or so in the acid to get the final finish. Save Comment CaiLei. Share More sharing options. This all depends on how much bubbling you have. Damascus etching is completed with either ferric chloride or muriatic acid. I etch my damascus blades in ferric chloride that I warm up a bit (around 160 F) however . Originally there was a method used in middle eastern sword making, but it has been lost since the 16th century. Need help with etching Damascus. What is Etching Damascus Blades? Muriatic acid needs no dilution. How to etch damascus. 3. I have a Damascus blade that's about perfect but I'm not sure how I'm supposed to etch it without ferric chloride. michiganroadkill. Here is my little jar filled with Muriatic acid. The near side steel pictured is a blend of 1085, 15-n-20 (nickel . You can make a reasonable facsimile of ferric by dissolving steel . Complete etches in a well ventilated space and wear gloves, eye protection, and an apron or old clothes. The bolsters are each suspended by a thin wire and allowed to etch in the acid. Can you etch Damascus steel with muriatic acid? What is an acid etched blade? . In order to bring out the beautiful patterns in the steel, it must be chemically etched. I never lay the blade flat because one side will etch faster. Either is effective. Found the internet! No matter how effective it is. It looks good, but provides little function. It is an ultra high carbon steel that achieved liquid state which should, theoretically, allow you to get a . Cover the edges of the steel. Before you begin, check the expiration date on your acid of choice to . By far, the best way too pickle blades is with white vinegar, just be sure and degrease them first. Share Facebook; Twitter; Linkedin; copy link. How to Etch Stainless and Carbon Damascus Steel Step 1: Sanding Bring your Damascus to a 400 to 600 grit finish. For ferric acid, keep the particle size between 400 and 600. The basic process is as follows: After heat treating, bring your Damascus to a 400 to 600 grit finish. That is why I recommended you dilute the HCl way down with water, Michael. For the Fe, you get some very fine steel wool and dissolve it in the Muriatic until no more will take. Close. Etching Damascus is a fairly straight forward process that can enhance the appearance of a Damascus blade. Wash your piece with alcohol and pat it dry with a clean rag. ferric acid etching damascus steel ferric acid etching damascus steel. Damascus Knife Blank Acid Etching Etching of Damascus is done after manufacturing or grinding of the blank to bring out the contrasting steel patterns. Etch in Muriatic Acid from the local hardware store. etching damascus with muriatic acid. You can make a reasonable facsimile of ferric by dissolving steel wool in muriatic acid. Update For this webisode we are etching 3 damascus knife blades and 4 clips. Traditionally, most knife companies use acid etching to enhance the visual aesthetic of their differential heat treatment, or to distinguish different layers of steel in a Damascus blade. The rib on the gun I'm doing has the fine checkered pattern on it. When I etch damascus I use muriatic acid. Polish, and enjoy! by Levi Alston. I tried Sulphuric acid (battery acid), Muriatic acid (swimming pool), and for these pieces, I used Ferric Chloride (copper etch mordant). What products are often used? Can you etch Damascus steel with muriatic acid? If you have to do it again. I sanded off the scrapes and polished up the light but in the process the etching was made even less. Step 1: Polish. Etching Damascus is a fairly straight forward process that can enhance the appearance of a Damascus blade. Hey Drew, when rusting and etching should the rib be protected? 2. Posts: 4,686. western michigan. Posted by 3 days ago. It is done by submerging the blade in an acid. Traditionally, most knife companies use acid etching to enhance the visual aesthetic of their differential heat treatment, or to distinguish different layers of steel in a Damascus blade. If you're using muriatic acid, you can bring the Damascus up to 1200 grit, or you can leave it at 400 grit. For ferric acid, keep the grit between 400 and 600. In your well-ventilated area, mix together one part muriatic acid to two parts hydrogen peroxide in a container that's big enough to fit the whole blade. It is AWESOME. M. Sure, you can etch steel with hydrochloric acid; e.g. The hardware store wasn't going to be very helpful in the . How to etch damascus. Method 1Method 1 of 2:Preparing the Steel for Etching. Campfire Guide. The acid etching will need to be done outside or in a well-ventilated area, and you should wear rubber gloves and goggles from here on out. hakoniwa explorer plus wiki By On 9, 2022. Etching. I'll time it for five minutes then neutralize and clean. etching damascus with muriatic acid. The art form has resurfaced in about 1973 by a blade-smith William F. Moran. . Etching Damascus - Mike Carter demonstrates how to acid etch Damascus knife blades to reveal the pattern in the steel; However, the moros have been etching their damascus moro kris and barong for centuries with citrus acid. 0 following Joined November 2019; Follow. Don't mess with muriatic acid! No Ferric Chloride anywhere in sight. Hydrochloric or Muriatic acid on Damascus . If you use muriatic acid, you can bring Damascus up to 1200 grit, or you can leave it 400 grit. Steven Penner Joined Jan 29, 2006 Messages 606 Jun 4, 2013. HCl works well, the trick is to dissolve it, since it's normally sold in concentrations of around 30%. With ferric acid, keep grit between 400 and 600. 0. Select the acid you'll use to etch the steel. always stand it up point down in a graduated cylinder. View. 1 Klinge / Edelstahl tumbled 3,25 mit Hndel 1x pro Bestellung . 12771 Mr.FATMAN () Wolfman Leather Barber Hat/5213024 Make a transfer of your design on the steel surface. as per: Cancel. what is letter naming fluency. Most people use it cold, which is very slow. These are made from Swedish Damasteel, a very high quality steel that I really enjoy working with. What products are often used? Making your own etchant: Fun for the whole family! If you recall, the bolsters for the Bobcat are made out of Damasteel, which is a pattern welded steel (Damascus). Immerse the steel in an etching acid bath. When someone feels their ferric chloride batch has "gone bad", you can add a tablespoon or so of muriatic acid and regenerate it. Press question mark to learn the rest of the keyboard shortcuts . Dunk it in the acetone again then allow to dry. STEP 1: STARTING Bring your Damascus at the end of grit 400 to 600. Keep it submerged for 10 to 15 minutes. I have used very dilute Muriatic (about .5 to 1%) to brown barrels (boil if you want black) and about 5 to 10% would be strong enough to use as echant depending . Close. How is it done? Acid etching Damascus I've been experimenting on some Damascus I'm using for knife projects with different acids to bring up the patterns. as per: Cancel. Dilute it about 4:1 water to acid. Be extra careful at this stage not to touch it! Sure, you can etch steel with hydrochloric acid; e.g. Then I remembered I'd been thinking of switching to re-usable etchant, created on the bench using muriatic acid (the store name for hydrochloric acid, HCl, used for cleaning swimming pools). Follow. Muriatic Acid, Ferric Chloride, Radio Shack PCB Etchant (Computer board etching solution) and I have he To warm your acid more quickly, the best method is to place the container of acid into a large bowl of warm . Neutralize the Damascus steel thoroughly after etching with bicarbonate soda to avoid further etching/corrosion. Press J to jump to the feed. I am looking for some input before I go ahead and do some additional etching on a flashlight of mine. Muriatic Acid is, I believe dilute Hydrochloric Acid but IMHO Muriatic is still a bit strong to use, you can dilute it, just remember to add the acid to water not the other way around. Also asked, does muriatic acid etch aluminum? Heating the acid solution will increase the corrosion rate also. Will muriatic acid be abel . Share . Damasteel is a powdered metallurgy stainless damascus steel. It is done by submerging the blade in an acid. expedia cancellation protection; badflower ghost spotify 2nd of two methods: etching the steel Select the picture to be etched into the steel. The HCL (hydrochloric acid) is commonly used in a diluted form called Muriatic Acid for PH balancing in pools. a no no. You can etch stainless steel, mild steel, or high-carbon steel. 2. Damascus etching is completed with either ferric chloride or muriatic acid. View. The look of the metal is due to pattern-welding steel, acid etched, and is the modern method to produce so called "Damascus steel". lots of bubbles = less time. Remove the Damascus from the acid and dip it in a bath of baking soda and distilled water to neutralize the acid. #5. I have a damascus that had very light damascus etching and also some scrape looking marks. Do not buff before etching! In this video we show our new and improved process on how to etch the steel aft. Be sure to always wear the appropriate protective gear when you're working with acid. We started out using Ferric Chloride, but for this steel I didn't like it at all. Follow. What is an acid etched blade? 0 following Joined November 2019; Follow.